ROHS ApprovedPolyester Wire Enamel (BAWA 216)
- BAWA 216.35 is a class 130 modified polyester wire enamel.
- BAWA 216.35 has very high processing speed and high cut through as
compared to Standard Wire Enamels
- BAWA 216.35 is suitable for Die Horizontal M/C & felt
applications
- BAWA 216.35 is specially suitable for wires upto 0.05-1.0mm.
| PHYSICAL
PROPERTIES |
| Appearance |
Brown Coloured Liquid |
| Solid Content |
35 ± 1% |
| 1g/1800C/1h |
|
| * Viscosity |
55 - 80 |
| Flash Point |
400C |
| Compatibility with thinner |
1 : 1 |
* Viscosity by Ford Cup (B4) at 300C in
Sec.
| THERMAL
PROPERTIES |
| Heat Shock |
|
|
| 5d/1800C/ 30min |
OK |
--- |
| 6d/1800C/ 30min |
--- |
|
| Cut Through |
|
|
| 2800C / 5min |
--- |
OK |
| 2800C / 2min |
OK |
---- |
| ELECTRICAL
PROPERTIES |
| Break Down Voltage kV |
at RT |
10.5 |
8.0 |
|
 |
| PHYSICAL
PROPERTIES (also available with below properties) |
| SOLID CONTENT % (lg/1h/1800C)
|
VISCOSITY |
PROPOSED Machine |
| 30 ± 1 |
100-200 |
HORIZONTAL FELT |
| 35 ± 1 |
250-500 |
HORIZONTAL FELT |
| 42 ± 1 |
600-700 |
HORIZONTAL DIE |
| 45 ±1 |
2700-3500 |
HORIZONTAL DIE |
Viscosity by viscometer/Brook field at 230c
in cps.
| MECHANICAL
PROPERTIES |
| Diameter of Bare wire |
1.0 mm |
0.5mm |
| Build up of enamel |
0.070 mm |
0.065mm |
| Elongation |
36% |
32% |
| Flexibility |
|
|
| Mandrel Winding (15% pre stretch 1xd) |
OK |
OK |
| Jerk Test |
OK |
OK |
| Peel Test (nXd) |
160 - 180 |
---- |
| Abrasion (Av) (Unidirectional) |
12N |
8 N |
| CHEMICAL
PROPERTIES |
| Solvent Resistance |
| Pencil Hardness |
| Initial |
3h |
3h |
| Std. Solvent |
2h |
2h |
| Tan
Delta |
| Bending Point 0C
(Solid Block) |
100-115 |
100-115 |
|
Please note that all above mentioned values may be changed according to
the machine.
| RECOMMENDED THINNER |
Thinner W/E |
| PACKING : |
Bawa 216.35
Thinner W/E |
210 Kg in mild steel drums.
21 Kg in mild steel drums. |
| SHELF LIFE |
One year from date of manufacturing if
stored in sealed container at room temperature 25 0C). |
This information contained here is best to our knowledge. Company makes no
warranty of results and assurance, no obligations or liabilities for the use
of any products or process therin. This publication is not to be taken as a
license to operate under or recommendation to infringe upon any patents.
©